Primarily to provide recommendations concerning minimizing stress-corrosion cracking in wrought titanium alloy products.
The detailed recommendations are based on laboratory experience and reflect those design practices and fabrication procedures which should obviate in-service stress-corrosion cracking of wrought titanium alloy products.
It must be emphasized that while stress-corrosion cracking in service has been observed, the chemical environmental conditions have, in all instances, been unusual and, although it is possible to produce stress-corrosion cracking of titanium alloys under more common conditions as discussed in these recommendations, there have been few, if any, failures in such environments.
The detailed recommendations are based on laboratory experience and reflect those design practices and fabrication procedures which should obviate in-service stress-corrosion cracking of wrought titanium alloy products.
It must be emphasized that while stress-corrosion cracking in service has been observed, the chemical environmental conditions have, in all instances, been unusual and, although it is possible to produce stress-corrosion cracking of titanium alloys under more common conditions as discussed in these recommendations, there have been few, if any, failures in such environments.